上海龍津金屬材料有限公司-歡迎您！
用途：在WC-Co合金中加入鉭、鈮碳化物固溶體，可以改善合金的高溫硬度、高溫強度和抗氧化性能。
|
牌號 |
90:10 |
80:20 |
70:30 |
60:40 |
50:50 |
|
|
化學成分 |
Ta |
84.4±1.5 |
71.5±1.5 |
65.6±1.5 |
56.0±1.3 |
46.9±1.3 |
|
Nb |
8.85±1.0 |
21.0±1.0 |
26.6±1.2 |
35.0±1.0 |
44.3±1.5 |
|
|
T.C |
6.75±0.3 |
7.3±0.3 |
7.8±0.3 |
8.2±0.3 |
8.8±0.3 |
|
|
F.C |
≤0.15 |
≤0.15 |
≤0.15 |
≤0.15 |
≤0.15 |
|
|
雜質含量，%， |
Co |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
|
Mo |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
|
|
Si |
0.02 |
0.02 |
0.02 |
0.02 |
0.02 |
|
|
Fe |
0.15 |
0.15 |
0.15 |
0.15 |
0.15 |
|
|
Ni |
0.04 |
0.04 |
0.04 |
0.04 |
0.04 |
|
|
K |
0.008 |
0.008 |
0.008 |
0.008 |
0.008 |
|
|
Na |
0.008 |
0.008 |
0.008 |
0.008 |
0.008 |
|
|
Mn |
0.05 |
0.05 |
0.05 |
0.05 |
0.05 |
|
|
Sn |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
|
|
Ca |
0.01 |
0.01 |
0.01 |
0.01 |
0.01 |
|
|
Al |
0.0.15 |
0.0.15 |
0.0.15 |
0.0.15 |
0.0.15 |
|
|
N |
0.25 |
0.25 |
0.25 |
0.25 |
0.25 |
|
|
O |
0.2 |
0.2 |
0.2 |
0.2 |
0.2 |
|
|
Ti |
0.2 |
0.3 |
0.3 |
0.3 |
0.3 |
|
|
W |
0.2 |
0.35 |
0.35 |
0.35 |
0.35 |
|
|
Cr |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
|
|
粒度(ūm) |
1.0-3.5 |
|||||